FH-GE is an epoxy-based thermosetting powder coating,formulated to offer a good flowing out and
glossy finish ranging from semi to high gloss, it is suitable for indoor use as a decorative and protective
coating . GLOSS AND COLOR RANGE
 Gloss levels range from 40% to 90% at 60º .  Full color range is available. APPLICATION SCHEDULE
 Applied by electrostatic spraying gun that can provide negative tension of 60-80 kV.  Curing schedule :15 minutes at 180℃ (metal temperature )
 Optimal film thickness : 60 -90 um
POWDER PROPERTIES
 Specific gravity : 1.25 - 1.75 (depend on colors)
 Particle size distribution(Laser Particle size analyser) :Less than 5% above 100 um
50 – 65% above 32 um :
Average particle size : 35 - 45umFH-GE is an epoxy-based thermosetting powder coating,formulated to offer a good flowing out and
glossy finish ranging from semi to high gloss, it is suitable for indoor use as a decorative and protective
coating . GLOSS AND COLOR RANGE
 Gloss levels range from 40% to 90% at 60º .  Full color range is available. APPLICATION SCHEDULE
 Applied by electrostatic spraying gun that can provide negative tension of 60-80 kV.  Curing schedule :15 minutes at 180℃ (metal temperature )
 Optimal film thickness : 60 -90 um
POWDER PROPERTIES
 Specific gravity : 1.25 - 1.75 (depend on colors)
 Particle size distribution(Laser Particle size analyser) :Less than 5% above 100 um
50 – 65% above 32 um :
Average particle size : 35 - 45um

APPLICATION : Electrostatic spraying gun
FH-GE is an epoxy-based thermosetting powder coating,formulated to offer a good flowing out and
glossy finish ranging from semi to high gloss, it is suitable for indoor use as a decorative and protective
coating . GLOSS AND COLOR RANGE
 Gloss levels range from 40% to 90% at 60º .  Full color range is available. APPLICATION SCHEDULE
 Applied by electrostatic spraying gun that can provide negative tension of 60-80 kV.  Curing schedule :15 minutes at 180℃ (metal temperature )
 Optimal film thickness : 60 -90 um
POWDER PROPERTIES
 Specific gravity : 1.25 - 1.75 (depend on colors)
 Particle size distribution(Laser Particle size analyser) :Less than 5% above 100 um
50 – 65% above 32 um :
Average particle size : 35 - 45um

Substrate Preparation

Substrate should be free of grease, oil, dirt, fingerprints,drawing compounds, any contamination,and surface preparation treatments to ensure optimum adhesion and coating performance properties. The use of a chemical conversion coating prior to the application of a powder coating is strongly recommended.