Prosperities

Test Condition

Test Method

Value

 Unit

Melting Flow Rate

200°C/5kg

ISO 1133

5.0

g/10min

Density

ISO 1183

1.04

g/cm3

Water Absorption

ISO 62

<0.1

%

Molding Shrinkage

ISO 294

0.4-0.7

%

Tensile Strength

23°C

ISO 527

23

Mpa

Tensile Elongation

23°C

ISO 527

50

%

Flexural Strength

23°C

ISO 178

46

Mpa

Flexural Modulus

23°C

ISO 178

2260

Mpa

Izod Impact Strength

23°C

ISO 180

108

j/m

Rockwell Hardness

23°C

ASTMD-785

65

L

Vicat Softening Temp.

B10/oil

ISO 306

95

°C

Heat Distortion Temp.

1.82Mpa

ISO 75-2

79

°C

UL Flame Class Rating

UL 94

HB

Residual Monomer

<400

ppm max