Brightener for KCR-25 Hard Chromium Plating

1. Properties

1. With high cathode efficiency, it may be up to 23%-26%.

2. The current density even over 60A/dm2 is available.

3. The deposition speed for KCR-25 bath is 2-3 times faster than conventional hard chromium process.

4. It is chloride-free, the KCR-25 process dose not cause erosion of the workpiece in low current density area.

5. The micro-hardness of the plating is up to 950HV-1100HV100. 

6. The amount of the micro cracks of the plating may be up to 400/cm, so it improves the corrosion resistance ability of the plating.