RTV silicone rubber for mold making applications

RTV silicone rubber for mold making 

is primarily intended for poly resin crafts, PU crafts, PU resin crafts ,gypsum crafts ,unsaturated resin crafts, lighting and candles crafts ,plastic toy , stationery gifts crafts industry, a large statue Buddha, furniture, furniture decorative materials, statues Buddha, artifacts copied, building decoration materials, largescale cement mold, artificial fossils Factory, Europe component factory, 

simulation landscapes, animals and plants sculpture, sandstone crafts and so on.

RTV silicone rubber for mold making description

RTV silicone rubber  for mold making is white or red flowing liquid with general hardness of 22-50 shore A after curing. tin cured RTV silicone rubber  is a kind elastic silicon rubber mold which features with resistance to deformation, high-temperature, acid-alkali and expansion as well as high reproduction times, good tensile strength, tear strength and elongation.

FAQ. Why the RTV silicone rubber for mold making mold just can be reproduced for a few times?

It can be due to the following reasons: 

a. Adding too much silicone oil in to silicon rubber. Silicon oil is an additive which destroies the molecular weight of silicone rubber and reduce the tension and tear strength.

b. Using the silicon rubber with a high hardness to make molds for small sized products with delicate and intricate designs and the silicon rubber with a low hardness to makes molds for large sized products with simple designs. 

(Notes: we should choose the silicon rubber specifically according to the requirements of our products to avoid this problem.)

The proportions and reactions of the curing agent and the silicon as follows

a. Adding curing agent 1%, The RTV silicone rubber can still be operated within 2.5 hours and can be demoulded after 6-8 hours.

b. Adding curing agent 2%, The RTV silicone rubber can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.

c. Adding curing agent 3%,  The RTV silicone rubber can still be operated within 28 - 30 minutes and can be demoulded after 1.5-2 hours.

d. Adding curing agent 4%,  The RTV silicone rubber can still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours.

For more information, please feel free to contact Ms. Susie

Office No.: 0086-755-89212380

Mob: +86-18938867549

Skype: susie0017

Email: hysx(at)szrl(dot)net 

Welcome to our website www dot szrl dot net