1.0619 Precision Carbon Steel Investment Casting Bonnet For Valve Industrial

Quick Detail:

1. Carbon steel bonnet of a valve cast by lost wax Casting process;

2. Material: 1.0619;

3. Manufactured by Investment casting foundry in China;

5. Max size: 500x500X350mm;

6. Weight: 15kg;

7. Chemical composition tested by German spectrometer;

8. PED and ISO9001:2008 certificated;

9. NDT test can be operated.

Description:

1.0619(Carbon steel) lost wax castings for valve industries, weights up to 80kg;

We perform steel lost wax casting process in a wide range of alloys, please refer to below table for the most common material that Winnington cast:

Overview of Investment Casting (or) Lost Wax Method

1.TOOL MAKING

A wax injection mold is designed and built to produce castings per customer specifications.

2. WAX PRODUCTION

A wax pattern is produced from the wax injection mold.

3. PATTERN ASSEMBLY

Wax patterns are attached to gating system by hot knife.

4. SHELL MAKING

The pattern assembly is dipped into a ceramic slurry, coated with a refractory material and dried. The process is repeated until the desired thickness and strength is achieved.

5. DEWAXING

Using regulated steam pressure, an autoclave melts and remove the wax from the ceramic shells.

6.SHELL PREHEAT

High temperature ovens cure and preheat the ceramic shells before pouring.

7. CASTING

Pre-heated Ceramic cavities are poured with the molten metal.

8.KNOCK OUT

The ceramic shell is removed by vibration knocking and the cluster is cleaned.

9.CUT OFF

Castings are cut off from the gating system.

10.MACHINING,SURFACE FINISH,AND INSPECTION

After cut off and gate removal, all secondary finishing operations ar