Brand:-
Model:-
MOQ:-0 -
Specification
| Panel Thickness(mm) | 2mm-8mm |
| Aluminium Skin Thickness(mm) | 0.08mm-0.5mm |
| Width(mm) | 1220mm-2000mm |
| Length(mm) | 2440mm-8000mm |
Feature
-Light weight, high strength, extreme rigidity, superior impact resistance,
-excellent surface flatness and smoothness ,
-heat insulation, sound insulation, fire-resistance,
-acid-resistance, alkali-resistance, good weatherproofing and non-resonance
-various uniform colors ,can be easily processed and fabricated, quickly installed,
-elegant and magnificent, good flexibility fits various designs,
-easily maintenance, simply cleaning
Applications
※ Constructional exterior curtain walls;
※Decorative renovation for storey-added old buildings;
※ Indoors decoration for interior walls, ceilings, bathrooms, kitchens and balconies;
※ Advertisement board, display platforms and signboards;
※Wallboard and ceilings for tunnels;
※ Raw materials in industrial purpose;
※Materials used for vehicle and boat.
SGS Test report for 3mm polyester A.C.P
| Items | Standard index of quality product | Result |
| Appearance | Clean surface without swell,flaws.scrath and aberration | pass |
| aberration | ||
| Length: ± 3mm | 0mm~+1mm | |
| Width: ± 2mm | 0mm~+1mm | |
| Thickness: ±0. 2mm | 0mm~+0.14mm | |
| Deviation of dimension | Deviation of diagonal: ≤ 5mm | 0mm |
| Out of straight at sides: ≤ 1mm/m | 0.2mm/m | |
| Warp: ≤ 5mm/m | 1mm/m | |
| Thickness of coating | ≥ 16um | 17um （av.18 ） |
| Deviation of luster | ≤ 10 | 2.6 （ av.20 ） |
| Hardness of pencil | ≥ HB | 2H |
| Toughness of coating | ≤ 3T | 1T |
| Adhesive | Not less than Grade1 | Squaring off method of Grade 0 Grade 1marking method of rolling line |
| Impact strength | 50Kg.cm Without paint off and crack | Pass |
| Boiling water resistance | (Boiling for 2h without change) | Unchanged |
| Acid resistance | Immerse surface with2%HCI(v/v)for 24H without change | Unchanged |
| Oil resistance | Immerse surface with 20# engine oil for 24h without change | Unchanged |
| Solvent resistance | Clean 100 times with dimethylbenzene without change | Bottom unrevealed |
| Cleaning resistance | ≥ 10000 （ ≥ 10000 times without change） | Unchanged |
| Abrasion resistance Density of surface | Specified value: ± 0.5Kg/m 2 | 3.63Kg/m 2 |
| Bend strength | ≥ 60Mpa | 79.6Mpa |
| Flexuous modulus of elasticity | ≥ 1.5×10 4 Mpa | 2.19 × 10 4 Mpa |
| Through resistance | ≥ 5.0kN | 6.25kN |
| Cutting strength | ≥ 20.0Mpa | 25.7Mpa |
| 180 o peel strength | ≥ 5.0N/mm | 6.2N/mm |
| Resistance to change of temperature | -40 o C~80 o C 20 cycles without change | Unchanged |
| Heat deformation temperature | ≥ 95oC | 116 o C |
| Coefficient of heat expansion | ≤ 4.00×10 -5 oC -1 | 2.47 × 10 -5 o C -1 |