K10 Tungsten Carbide Rod Blanks with 6% Cobalt, Hardness 93.5 - 93.8 HRA

Description: 

Cemented carbide essentially consists of two main components: hard metal tungsten carbide (WC) and binding agent Co. Carbide contributes to high hardness property in a most important degree for hard metal WC, while cobalt maintains its relative high toughness at the high level of hardness. With Hot Isostatic Pressing sintering technique, cemented carbide material is fully consolidated by simultaneous application of heat and pressure, producing a close-to-full-density state. Consequently, the technique greatly optimizes rod’s quality, being more stable and reliable. 

- ISO Range: K10

- with 94% tungsten carbide, 6% cobalt 

- Made of 0.4 micron ultrafine TC powder

- Hardness: 93.5-93.8 HRA

- Bending strength: >3200 MPa

- Density: 14.8 g/cm3

- As sintered
                                            
- Dimension: unground fixed length bar in metric size

Specifications:

Solid rods- cut to length(Metric):

D	Tolerance of D	Length	D	Tolerance of D	Length
mm	(mm)	mm	mm	(mm)	mm
3.0	+0.2/+0.4	38.5	8.0	+0.2/+0.4	100
3.0	+0.2/+0.4	50	8.0	+0.2/+0.4	Contact Infomation Send Inquiry Company name:Jiangsu Hetian Technological Material Co., Ltd. Status:[Offline] [Send message] [Chat] Business contact:Miss. Voyonna. T (Ms.) Telphone: Mobile: Fax: Area: Caribbean Region-Bermuda Address:No.295, Qianluo Village, Dingshu Town, Yixing City, Jiangsu Zip:214000