1.Material: 95% Al2O3
2.Method of moulding: Thermal casting/dry press/ extrusion
3.Colour:white
4. Sintering temperature:1750oC
5.Material characteristics: HRA&ge 86 &rho&ge 3.6 resist acid and alkali
6.Surface finish: Ra0.4&simRa0.8&mum
7.Packing: pack with carton and ship with wooden case
8.Produce products according to molds or drawings provided.by the client and quote according the data of the products
9.The mould fee of the non-standard products: According the quotion of product.
95%/99%/99.7% Al2O3 Material Parameters:
Item | Test Condition | Unit&Symbol | 95%Alumina ceramics | 99%Alumina ceramics | 99.7%Alumina ceramics |
The main chemical ingredient |
|
| Al2O3 | Al2O3 | Al2O3 |
Bulk Density |
| g/cm3 | 3.6 | 3.89 | 3.96 |
Maximum Use Temperature |
|
| 1450°C | 1600°C | 1650°C |
Water absorption |
| % | 0 | 0 | 0 |
ROHS Hardness |
|
| ≥85 | ≥89 | ≥89 |
Flexural strength | 20° C | MPa (psi x 103) | 358 (52) | 550 | 550 |
Compressive Strength | 20° C | MPa (psi x 103) | 2068 (300) | 2600(377) | 2600(377) |
Fracture Toughness | K(I c) | Mpa m1/2 | 4-5 | 5.6 | 6 |
Coefficient of thermal expansion | 25-1000° C | 1X 10-6/°C | 7.6 | 7.9 | 8.2 |
Coefficient of thermal conductivity | 20° C | W/m °K | 16 | 30.0 | 30.4 |
Thermal Shock Resistance | Tc | °C | 250 | 200 | 200 |
Dielectricity constant | 1MHz.25°C |
| 9 | 9.7 | 9.7 |
Dielectric strength |
| ac-kV/mm (ac V/mil) | 8.3 (210) | 8.7 (220) | 8.7 (220) |
Volume Resistivity | 100°C | ohm-cm | > 1013 | > 1014 | > 1014 |