Model:304l
304L 2B STAINLESS STEEL
Introduction
304L is a low carbon 304 stainless steel variant, for welding applications. Lower carbon content makes it close to the weld heat affected zone to minimize carbide precipitation, and carbide precipitation may result in some environments,
stainless steel intergranular corrosion (weld erosion).
| Artical | steel for plates 304L 0.5mm thickness | ||||||
| Specification | 1000mm*2000mm,1219mm*2438mm or as your requirement | ||||||
| Surface | 2B | ||||||
| Type | plate | ||||||
| Thickness | 0.3mm~6mm | ||||||
| Mill | TISCO/ BAOSTEEL/ JISCO/ ZPSS | ||||||
| Packing | interleaving paper, kraft paper and wooden pallet or as your requirement | ||||||
| Payment terms | 30%T/T in advance, the balance against the B/L copy | ||||||
| 30%T/T in advance, the balance against the L/C at sight | |||||||
| 100%L/C at sight | |||||||
| Dilivery time | 10days after receving the deposit of T/T | ||||||
| 10days after receving the deposit of L/C original | |||||||
chemical properties
| Typical chemical composition | ||||
| % | 304 | 304L | 316 | 316L |
| C | 0-0.07 | 0-0.03 | 0.8 | 0.03 |
| Mn | 0-2.0 | 0-2.0 | 2 | 2 |
| Si | 0-1 | 0-1 | 0.75 | 0.75 |
| P | 0-0.05 | 0-0.05 | 0.045 | 0.045 |
| S | 0-0.02 | 0-0.02 | 0.03 | 0.03 |
| Cr | 17.5-19.5 | 17.5-19.5 | 16.0-18.0 | 16.0-18.0 |
| Ni | 8-10.5 | 8-10.5 | 10.0-14.0 | 10.0-14.0 |
| Mo | 2.00-3.00 | 2.00-3.00 | ||
| N | 0.1 | 0.1 | ||
| Fe | Balance | Balance | ||
Pysical properties
Tensile strength σb (MPa) ≥ 520
Conditions yield strength σ0.2 (MPa) ≥ 205
Elongation δ5 (%) ≥ 40
Section shrinkage ψ (%) ≥ 60
Hardness: ≤ 187HB; ≤ 90HRB; ≤ 200HV
Surface
Pictures of products
Mill test certificate
Interleaving
Packing
PVC
Application
.304L, Applied to grain boundary corrosion resistance requirements of the chemical, coal, petroleum industry, the open field machinery, building materials, heat resistant parts and difficult parts.
Stock picture
Workshop
All the above information is for reference , if you have any further questions please feel free to contact us.Your inquries will be warmly welcome.