Product features:
1, this product points A, B component packaging, are colorless transparent liquid, avoid light environment can save time.
2, silicon - oxygen (Si - O) key chain structure, so mainly by not easily by ultraviolet and ozone, no p-bond exists, decompose at high temperatures (or radiation) molecular bond doesn't break, can be in - 50 Degrees Celsius ~ 200 Degrees Celsius j in use for a long time. Van turn After 300 Degrees Celsius of intensifying test changes after seven days, not cracked, not sclerosis, colloid external force can be automatically healing after cracking.
3, colloid after curing thallose cellophane tape shows colorless, PPA and metal has a certain adhesion and sealing is good.
4, excellent electrical insulating performance and good sealing.
5, suitable for lens filling production high power LED.

Recommended process: Different packaging process, the proposal with different ratio, get better effect.
1, than by weight for A: B = 1: 1 proportion with glue, stirring 8 minutes.
2, vacuum TuoPao 10 minutes.
3, in injecting before, please will bracket and lens in 130 Degrees Celsius
Above preheated 60 minutes under except tide.
4, first 80 Degrees Celsius roast 1 hours to 120 Degrees Celsius temperature bake again 2 hours, segmentation curing can effectively solve the problem improve yield bubble.

Note
Production should calculate the amount of good match glue in operating time, must the glue used up. When with glue mixing must even, otherwise you will solidify not completely and affect the product performance. This product is a silastic products, use process should avoid contact with the material:
Organic tin compounds and other organic metal compounds;
Contain organic tin compounds silicone rubber;
Sulphur, more sulfur compounds, poly sulphone and other sulfur-containing materials;
Amine, ethyl carbamate fat or other contain amine materials;
Unsaturated hydrocarbons plasticizer;