Model:DBRS-125G(2X)LS
l
Volsun DBRS-125G(2X)LS, made of radiation cross-linked polyolefin, has excellent physicochemical and electrical properties. It can reliably insulate cable and wire splices and terminations, effectively protect soldered joint and provides good mechanical protection for wire harness in electronic, communications, automotive, shipping and aircraft manufacturing industries.
l Features
2 Shrink ratio：2:1
2 Flexible、flame retardant、environmentally friendly、low temperature shrinkable
2 Shrink temperature：65℃～95℃
2 Continuous operating temperature：-55℃～125℃
2 RoHS compliant
2 Standard color：black
l Technical Performance
| Property | Typical data | Test method/condition |
| Tensile strength | ≥12MPa | ASTM D 2671 |
| Elongation at break | ≥400% | ASTM D 2671 |
| Tensile strength after heat aging | ≥11MPa | 158℃×168h |
| Elongation after heat aging | ≥200% | 158℃×168h |
| Longitudinal change | -5%～+5% | UL 224 |
| Flammability | VW-1 | UL VW-1 |
| Voltage withstand（rated voltage 600V） | 2500V，1min no breakdown | UL 224 |
| Heat shock | No cracks，no dripping | UL 224，250℃×4h |
| Dielectric strength | ≥20kv/mm | IEC 243 |
| Volume resistivity | ≥1014Ω.cm | IEC 93 |
l
l Dimension
| Size(inch) | As supplied ID(mm) (min.) | After full recovery(mm) | Standard package (m/spool) | |
| IAs supplied ID(max.) | wWall thickness(min.) | |||
| 1/16 | 1.6 | 0.80 | 0.50 | 200 |
| 3/32 | 2.4 | 1.20 | 0.50 | 200 |
| 1/8 | 3.2 | 1.60 | 0.50 | 200 |
| 3/16 | 4.8 | 2.40 | 0.50 | 100 |
| 1/4 | 6.4 | 3.20 | 0.60 | 100 |
| 5/16 | 8.0 | 4.00 | 0.60 | 100 |
| 3/8 | 9.5 | 4.80 | 0.60 | 100 |
| 1/2 | 12.7 | 6.40 | 0.60 | 50 |
| 5/8 | 16.0 | 8.00 | 0.60 | 50 |
| 3/4 | 19.1 | 9.50 | 0.80 | 50 |
| 1 | 25.4 | 12.70 | 0.90 | 50 |
| 1-1/4 | 31.8 | 15.90 | 0.90 | 50 |
| 1-1/2 | 38.1 | 19.10 | 1.00 | 50 |
| 2 | 50.8 | 25.40 | 1.10 | 50 |
Note: non standard dimensions and packages are also available on request