Material & Feature &Application
Heat Shrinkable Tube forms by chemical cross-linked (byradiation) thermally stabilized flame retarded polyolefin. It has excellent un-flammability, flexibility, and insulation. The shrinking temperature is very low and it can shrink very quickly.

It is widely used for various electric insulation and bonding of cales and connectors and applied for connecting end handling of electric wire, insulating and harness of electric wire.

Shrink temperature: 90
Temperature Renge: -55 to 125
Radial Shrinking Ratio: >50%
Longitudinal shrinking ratio: <5%
Tensile Strength: >14Mpa
Aging 158.0± 1.0° Lays aside for 7 days 7Days Air Cren at158.0± 1.0 Through
134.0± 1.0° Lays aside for 60 days 60Days Air Cren at134.0± 1.0
Tensile Stength after Aging: >10Mpa
Elongation after Aging: >200%
Volume Resistivity: >10??@cm
Dielectric strength: >25KV/mm
Flammability: VW-1