Place of Origin: Guangdong China (Mainland)
Brand Name: Lianhuan brand
Model Number: Silicone rubber
Color: Any
Viscosity: Low
Tensile Strength: Strong
Tear strength: High
Size stability: Good
Reproduction times: High
Elongation: High
Linear shrinkage rate: Low
Anti-scar: -50-180° C
Stripping the gender: Good

Packaging & Delivery
Packaging Detail:
Wooden cases or according to your request
Delivery Detail
3days after payment

Application:
Silicone rubber is mainly applicable for artficial stone silicone rubber mold making, mirror frames silicone rubber mold making. Toy crafts silicone rubber mold making, relief sculpture silicone rubber mold making, artwork silicone rubber mold making. Fireplace silicone rubber mold making, poly crafts, resin craftworks, lightings, candles, etc, and fabrication of precision silicone rubber mold making.

Silicone rubber for soap mold making descriptions:
Silicone rubber are general called two-component room temperature vulcanization silicone rubber with excellent fluidity and good operational perormance, an elastic silicone rubber mold will be obtained with resistance to deformation, high-temperature, acid and alkali and expansion.

1. Silicone rubber for soap mold making: Flowable liquid silicone and curing agent.
2. Silicone rubber for soap moldl making cures at ROM temperature within2-4 hours.
3. An exceptional fluidity and good operability, easy to demold.
4. Good tensile and tear strength, low shrinkage.
5. High duplication times.

ConDENSATION CURE RTV-2 MOLDMAKING SILICO
Model: RTV M 20 silicone rubber
Appearance: White
Viscosity (CS): 20, 000
Hardness (Shore A): 20-22
Tensile strength(MPA) ≥ 2.8
Tear strength (kN /m): ≥ 2.0
Elongation break(%): ≥ 500
Retractility (%): ≤ 0.2
Curing agent mixed rate (%): 2
Operate time (min): 30
Curing time (hours): 2-4

Model: RTV M 25 silicone rubber
Appearance: White
Viscosity (CS): 21, 000
Hardness (A): 25-26
Tensile strength(MPA ) ≥ 3.0
Tear strength (KN/M): ≥ 2.5
Elongation break(%): ≥ 480
Retractility (%): ≤ 0.2
Curing agent mixed rate (%): 2
Operate time (min): 30
Curing time (hours): 2-4

Model: RTV M 30 silicone rubber
Appearance: White
Viscosity (CS): 30, 000
Hardness (A): 30-32
Tensile strength(MPA ) ≥ 3.8
Tear strength (KN/M): ≥ 28
Elongation break(%): ≥ 460
Retractility (%): ≤ 0.2
Curing agent mixed rate (%): 2
Operate time (min): 30
Curing time (hours): 2-4

Model: RTV M 330 silicone rubber
Appearance: Translucent
Viscosity (CS): 20, 000
Hardness (Shore A): 20-22
Tensile strength(MPA) ≥ 3.2
Tear strength (kN /m): ≥ 2.0
Elongation break(%): ≥ 460
Retractility (%): ≤ 0.2
Curing agent mixed rate (%): 2
Operate time (min): 30
Curing time (hours): 2-4

Model: RTV M 50 silicone rubber
Appearance: Off-white
Viscosity (CS): 39, 000
Hardness (Shore A): 43-45
Tensile strength(MPA) ≥ 2.8
Tear strength (kN /m): ≥ 1.8
Elongation break(%): ≥ 380
Retractility (%): ≤ 0.2
Curing agent mixed rate (%): 2
Operate time (min): 30
Curing time (hours): 2-4