Major Functions of RH-800 Laser Cladding System
1. Scope of Application
Rapid repairing of defects on large, medium and small size variousmachinery parts;
Repairing of defects on matrices of various materials andhardness;
Cladding with various metals and non-metal materials like tungstencarbide and ceramic powder, etc;
Surface modification of matrix, such as acid resistance, alkaliresistance, heat resistance, and wear-resistance, etc.
2. Cladding Speed is Φ 3.5mm× (0-14)Hz/S.
3. Cladding Thickness
Thickness cladding metal powder once can reach 0.1mm-1.0mm, whilethickness cladding sheet metal once can reach 0.1mm-0.6mm. Fusioncasting can be repeated to increase thickness
4. RH-800 Laser Cladding System can be equipped with optical fiberof 0-200m, which is convenient for long-distance non-contact metalrepairing.
The following are additional functions.

Laser Welding
1. Penetration Welding
When no padding welding 3mm double layer metal plate, the weldinglayers shall be metallurgically bonded, and there shall be not anyweld mark on reverse side of welding spot. It's fit for welding ofthose reverse side of welding layer requires smooth finish or withcoating or with inflammables. Matrix shall be nondeforming afterwelding.
2. Autogenous Welding
When butt autogenous welding metal plates below 10mm, it shall bemetallurgical bonding, welding
Spots shall be continuous and uniform, and welding seam shall beneat and no surface flash.
3. Slugging
metal powder, metal wire and sheet metal can be taken as weldingmaterial to weld various metals, and matrix shall be nondeformingafter welding.
4. Thin-wall Welding
It can weld metallic strap and metal plate above 0.1mm in variousmethods. Matrix shall be nondeforming after welding.

Laser Cutting
It can cut automatically metal plates below 10mm. The cut shall beuniform and neat, and the speed shall surpass linear cutting.
Laser Quenching
By scanning with facula on metal surface, quenching of which can beaccomplished. The quenched surface shall be uniform, and quenchingposition shall be accurate. Hardness of 45 steel after surfacequenching by laser shall be HRC50-55