Description:
It is suitable for furniture making and decoration , strongsticking strength for PVC board , Fiber Board.productdescription
White latex also called the polyvinyl acetate adhesive , by acetic acid and ethylene is vinyl acetate synthesis. Temperature curing, curing faster, adhesive strength is higher, adhesive layer has good toughness and durability and not easy to aging.
Specification Data :
Test Item | Unit | Test Result |
Appearance | / | Ivory Yellow , no coarse particle |
Adhesive | Map''s | 26000 |
Non-volatile Matter | % | 25 |
Compressive Shear Strength | Map | 3.8 |
Ash Specification | % | 0.3 |
Ph | / | 6 |
Free Formaldehyde | g/kg | 0.6 |
Benzene | g/kg | / |
Toluene & Xylene | g/kg | / |
Volatile Organic Content | g/L | 25 |
physical property
Relation of temperature , humidity and pressurized time .
Table 1
Temperature | 5-15°C | 15-25°C | 25-35°C or Above |
Humidity | 40-60% | 40-60% | 40-60% |
Pressurized Time | 8-12 hours | 4-6 hours | 2-4 hours |
Table 2
Temperature | 5-15°C | 15-25°C | 25-35°C or Above |
Humidity | <=40 | <=40 | <=40 |
Pressurized Time | 8-10 hours | 4-5 hours | 2-3 hours |
Table 3
Temperature | 5-15°C | 15-25°C | 25-35°C or Above |
Humidity | >=85% | >=85% | >=85% |
Pressurized Time | 24-28 hours | 20-22 hours | 16-20 hours |
feature:
1. Low VOC
2. Room temperature curable .
3. Fast dry
4. Strong sticking strength
5. Good initial adhesive
Application
1. Surface Preparation : make the surface dry , clean and smooth .
2. Mixed evenly : Mixed it evenly before use .
3. Apply latex
4. Pressurized evenly for 1 hours or above . It could not application until pressure relief for 24 hours